Interfacial Fermi level and surface band bending in Ni/semi-insulating GaAs contact

Abstract

For nickel on the chemically clean surface of undoped semi-insulating GaAs at room temperature, an upward surface band bending of 0.062 eV and a barrier height of 0.690 eV have been observed by the photovoltage and the internal photoemission techniques, respectively. The observed surface band bending is in excellent agreement with its predicted value, and the observed barrier height also agrees very well with its value from the very careful analysis of reversed I-V data. It has been determined that the interfacial Fermi level lies at 0.690 eV below the GaAs conduction band minimum at the interface. The interfacial Fermi level is found to coincide with the energy level of the EL2 native defect, indicating the importance of the EL2 in the Fermi level pinning at the interface. © 1995 American Institute of Physics.