TitleIn vitro evaluation of the bonding durability of self-adhesive resin cement to titanium using highly accelerated life test
Authors
KeywordsBonding durability
Cyclic impact load
Highly Accelerated Life Test
Resin cement
Titanium
Issue Date2011
PublisherNihon Shika Riko Gakkai. The Journal's web site is located at http://www.jsdmd.jp/allpdf.html
Citation
Dental Materials Journal, 2011, v. 30 n. 6, p. 837-844 How to Cite?
AbstractThe purpose of this in vitro study was to evaluate the bonding durability of three self-adhesive resin cements to titanium using the Highly Accelerated Life Test (HALT). The following self-adhesive resin cements were used to bond pairs of titanium blocks together according to manufacturers' instructions: RelyX Unicem, Breeze, and Clearfl SA Luting. After storage in water at 37°C for 24 h, bonded specimens (n=15) immersed in 37°C water were subjected to cyclic shear load testing regimes of 20, 30, or 40 kg using a fatigue testing machine. Cyclic loading continued until failure occurred, and the number of cycles taken to reach failure was recorded. The bonding durability of a self-adhesive resin cement to titanium was largely infuenced by the weight of impact load. HALT showed that Clearfl SA Luting, which contained MDP monomer, yielded the highest median bonding lifetime to titanium.
Persistent Identifierhttp://hdl.handle.net/10722/143729
ISSN
2023 Impact Factor: 1.9
2023 SCImago Journal Rankings: 0.589
ISI Accession Number ID
References

 

DC FieldValueLanguage
dc.contributor.authorLin, Jen_HK
dc.contributor.authorShinya, Aen_HK
dc.contributor.authorGomi, Hen_HK
dc.contributor.authorMatinlinna, JPen_HK
dc.contributor.authorShinya, Aen_HK
dc.date.accessioned2011-12-21T08:47:27Z-
dc.date.available2011-12-21T08:47:27Z-
dc.date.issued2011en_HK
dc.identifier.citationDental Materials Journal, 2011, v. 30 n. 6, p. 837-844en_HK
dc.identifier.issn0287-4547en_HK
dc.identifier.urihttp://hdl.handle.net/10722/143729-
dc.description.abstractThe purpose of this in vitro study was to evaluate the bonding durability of three self-adhesive resin cements to titanium using the Highly Accelerated Life Test (HALT). The following self-adhesive resin cements were used to bond pairs of titanium blocks together according to manufacturers' instructions: RelyX Unicem, Breeze, and Clearfl SA Luting. After storage in water at 37°C for 24 h, bonded specimens (n=15) immersed in 37°C water were subjected to cyclic shear load testing regimes of 20, 30, or 40 kg using a fatigue testing machine. Cyclic loading continued until failure occurred, and the number of cycles taken to reach failure was recorded. The bonding durability of a self-adhesive resin cement to titanium was largely infuenced by the weight of impact load. HALT showed that Clearfl SA Luting, which contained MDP monomer, yielded the highest median bonding lifetime to titanium.en_HK
dc.languageengen_US
dc.publisherNihon Shika Riko Gakkai. The Journal's web site is located at http://www.jsdmd.jp/allpdf.htmlen_US
dc.relation.ispartofDental Materials Journalen_HK
dc.subjectBonding durabilityen_HK
dc.subjectCyclic impact loaden_HK
dc.subjectHighly Accelerated Life Testen_HK
dc.subjectResin cementen_HK
dc.subjectTitaniumen_HK
dc.titleIn vitro evaluation of the bonding durability of self-adhesive resin cement to titanium using highly accelerated life testen_HK
dc.typeArticleen_HK
dc.identifier.openurlhttp://library.hku.hk:4550/resserv?sid=HKU:IR&issn=0287-4547&volume=30&spage=837&epage=844&date=2011&atitle=In+vitro+evaluation+of+the+bonding+durability+of+self-adhesive+resin+cement+to+titanium+using+highly+accelerated+life+testen_US
dc.identifier.emailMatinlinna, JP:jpmat@hku.hken_HK
dc.identifier.authorityMatinlinna, JP=rp00052en_HK
dc.description.naturelink_to_OA_fulltext-
dc.identifier.doi10.4012/dmj.2011-054en_HK
dc.identifier.pmid22123007-
dc.identifier.scopuseid_2-s2.0-82855176872en_HK
dc.identifier.hkuros198028en_US
dc.relation.referenceshttp://www.scopus.com/mlt/select.url?eid=2-s2.0-82855176872&selection=ref&src=s&origin=recordpageen_HK
dc.identifier.volume30en_HK
dc.identifier.issue6en_HK
dc.identifier.spage837en_HK
dc.identifier.epage844en_HK
dc.identifier.isiWOS:000299863100007-
dc.publisher.placeJapanen_HK
dc.identifier.scopusauthoridLin, J=36519085300en_HK
dc.identifier.scopusauthoridShinya, A=35604258300en_HK
dc.identifier.scopusauthoridGomi, H=36631983000en_HK
dc.identifier.scopusauthoridMatinlinna, JP=6602419428en_HK
dc.identifier.scopusauthoridShinya, A=7004292632en_HK
dc.identifier.issnl0287-4547-

Export via OAI-PMH Interface in XML Formats


OR


Export to Other Non-XML Formats