Article: Failure cause analyses on the material of deaerator/surgas stripper in synthetic ammonia installation

TitleFailure cause analyses on the material of deaerator/surgas stripper in synthetic ammonia installation
Authors
Lu, WJin, GXXu, DXu, GYWu, YS
KeywordsAustenitic Stainless Steel
Leakage
Pitting
Stress Corrosion
Issue Date2010
Citation
Corrosion And Protection, 2010, v. 31 n. 7, p. 570-573 How to Cite?
AbstractFor the leakage accident in the cylindrical shell's material of the deaerator/sourgas stripper in the synthetic ammonia equipmeut, the chemical composition, microstructure, corrosion condition, crack and fracture of the cylindrical shell's material were analyzed. The results show that the material of the cylindrical shell is 316L stainless steel, and the failure of the material was due to stress corrosion cracking which was induced by the regional enrichment of Cl - in the cylindrical shell to cause pitting consequently. Besides, the acid media, such as H 2S, CO 2, HCOOH and CO, O 2 in the cylindrical shell had accelerated the propagation of stress corrosion cracking. A corresponding improvement measure of using duplex stainless steel is suggested.
Persistent Identifierhttp://hdl.handle.net/10722/168517
ISSN
1005-748X
2023 SCImago Journal Rankings: 0.111
References
References in Scopus

 

DC FieldValueLanguage
dc.contributor.authorLu, Wen_US
dc.contributor.authorJin, GXen_US
dc.contributor.authorXu, Den_US
dc.contributor.authorXu, GYen_US
dc.contributor.authorWu, YSen_US
dc.date.accessioned2012-10-08T03:19:54Z-
dc.date.available2012-10-08T03:19:54Z-
dc.date.issued2010en_US
dc.identifier.citationCorrosion And Protection, 2010, v. 31 n. 7, p. 570-573en_US
dc.identifier.issn1005-748Xen_US
dc.identifier.urihttp://hdl.handle.net/10722/168517-
dc.description.abstractFor the leakage accident in the cylindrical shell's material of the deaerator/sourgas stripper in the synthetic ammonia equipmeut, the chemical composition, microstructure, corrosion condition, crack and fracture of the cylindrical shell's material were analyzed. The results show that the material of the cylindrical shell is 316L stainless steel, and the failure of the material was due to stress corrosion cracking which was induced by the regional enrichment of Cl - in the cylindrical shell to cause pitting consequently. Besides, the acid media, such as H 2S, CO 2, HCOOH and CO, O 2 in the cylindrical shell had accelerated the propagation of stress corrosion cracking. A corresponding improvement measure of using duplex stainless steel is suggested.en_US
dc.languageengen_US
dc.relation.ispartofCorrosion and Protectionen_US
dc.subjectAustenitic Stainless Steelen_US
dc.subjectLeakageen_US
dc.subjectPittingen_US
dc.subjectStress Corrosionen_US
dc.titleFailure cause analyses on the material of deaerator/surgas stripper in synthetic ammonia installationen_US
dc.typeArticleen_US
dc.identifier.emailLu, W:luwei@hku.hken_US
dc.identifier.authorityLu, W=rp00754en_US
dc.description.naturelink_to_subscribed_fulltexten_US
dc.identifier.scopuseid_2-s2.0-79953275261en_US
dc.relation.referenceshttp://www.scopus.com/mlt/select.url?eid=2-s2.0-79953275261&selection=ref&src=s&origin=recordpageen_US
dc.identifier.volume31en_US
dc.identifier.issue7en_US
dc.identifier.spage570en_US
dc.identifier.epage573en_US
dc.identifier.scopusauthoridLu, W=27868087600en_US
dc.identifier.scopusauthoridJin, GX=7401563177en_US
dc.identifier.scopusauthoridXu, D=37094252300en_US
dc.identifier.scopusauthoridXu, GY=7404264740en_US
dc.identifier.scopusauthoridWu, YS=37094372500en_US
dc.identifier.issnl1005-748X-

Export via OAI-PMH Interface in XML Formats

OR

Export to Other Non-XML Formats