Undoped gallium antimonide studied by positron annihilation spectroscopy

Abstract

Positron lifetime spectroscopy has been used to study the vacancy type defects in undoped gallium antimonide. Temperature dependent positron trapping into the VGarelated defect having a characteristic lifetime of 310ps was observed in the as-grown sample. The lifetime data were well described by a model involving the thermal ionization (0/-) of the VGa-related defect and its ionization energy was found to be E(0/)=83meV. For the electron irradiated sample, the VGa-related defect with lifetime of 310ps that was found in the non-irradiated samples was also identified. Moreover, another lifetime component (280ps) was only observed in the electron irradiated sample but not in the non-irradiated sample. It was also attributed to the V Ga-related defect. The two identified VGa-related defects should have different microstructures because of their difference in characteristic lifetimes. The 280ps component remains thermally stable after the 500°C annealing while the 310ps component anneals at 300°C.