Experimental novel silane system in adhesion promotion between dental resin and pretreated titanium

Abstract

Five silane blends were evaluated as experimental adhesion-promoter primers. First, five organosilane monomers (silicon esters), 3-acryloxypropyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-glycidoxypropyltrimethoxysilane, tetrakis-(2-ethyloxyethoxy)silane and bis-[3-(triethoxysilyl)propyl]tetrasulfide, were diluted to 1% (v/v) and blended with a non-functional cross-linking silane, 1,2-bis-(triethoxysilyl)ethane (1%), in 95% ethanol. After activation, each blend was applied to silica-coated Ti coupons. A resin based on bis-phenol-A-diglycidyldimethacrylate was then bonded and photo-polymerized as stubs to the pretreated Ti coupons. Half of the specimens were stored in dry conditions and half were artificially aged by thermo-cycling. The primers containing 3-acryloxypropyltrimethoxysilane and 3-methacryloxypropyltrimethoxysilane produced significantly higher shear bond strength values than the control silane, a standard pre-activated product used in clinical dentistry. © Springer Science+Business Media B.V. 2010.